Characteristics of La0.8Sr0.2Ga(0.8x)Mg0.2O3-delta (x=0.85, 0.9, 0.95, 1) electrolytes formed from powders prepared by spray pyrolysis
- Authors
- Jung, Dae Soo; Kim, Jung Hyun; Koo, Hye Young; Ko, You Na; Cho, Yoon Ho; Lee, Jong-Heun; Kang, Yun Chan
- Issue Date
- 10월-2011
- Publisher
- KOREAN ASSOC CRYSTAL GROWTH, INC
- Keywords
- Spray pyrolysis; Solid electrolyte; Nano powder; Fuel cells
- Citation
- JOURNAL OF CERAMIC PROCESSING RESEARCH, v.12, no.5, pp.572 - 577
- Indexed
- SCIE
SCOPUS
KCI
- Journal Title
- JOURNAL OF CERAMIC PROCESSING RESEARCH
- Volume
- 12
- Number
- 5
- Start Page
- 572
- End Page
- 577
- URI
- https://scholar.korea.ac.kr/handle/2021.sw.korea/111498
- ISSN
- 1229-9162
- Abstract
- La0.8Sr0.2Ga(0.8x)Mg0.2O3-delta (LSGM) (x = 0.85, 0.9, 0.95, 1) precursor powders were prepared by spray pyrolysis from spray solutions with various Ga contents. The pellets fired at 1400 degrees C had dense structures without pores, irrespective of the Ga content of the powders. The grain sizes of the pellets formed from powders with low Ga contents were larger than those of the pellets formed from powders with stoichiometric Ga contents. At firing temperatures of 1300 degrees C and 1400 degrees C, phase-pure LSGM pellets were obtained from powders with a stoichiometric amount of 85 at.% Ga (x = 0.85), as was evident from the results of crystal structure analysis. An orthorhombic-rhombohedral phase transition occurred in the pellets formed from powders with stoichiometric amounts of 95 at.% (x = 0.95), and 85 at.% (x = 0.85) Ga at a firing temperature of 1400 degrees C. The conductivities of LSGM with orthorhombic and rhombohedral structures sintered at 1400 degrees C were 0.007 S/cm and 0.022 S/cm, respectively, at a low measurement temperature of 600 degrees C.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > Department of Materials Science and Engineering > 1. Journal Articles
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.