Growth Behavior and Electrical Properties of a (Na0.5K0.5) NbO3 Thin Film Deposited on a Pt/Ti/SiO2/Si Substrate Using RF Magnetron Sputtering

Authors
Kang, Lee-SeungKim, Bo-YunSeo, In-TaeSeong, Tae-GeunKim, Jin-SeongSun, Jong-WooPaik, Dong-SooHwang, InrokPark, Bae HoNahm, Sahn
Issue Date
7월-2011
Publisher
WILEY
Citation
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, v.94, no.7, pp.1970 - 1973
Indexed
SCIE
SCOPUS
Journal Title
JOURNAL OF THE AMERICAN CERAMIC SOCIETY
Volume
94
Number
7
Start Page
1970
End Page
1973
URI
https://scholar.korea.ac.kr/handle/2021.sw.korea/112148
DOI
10.1111/j.1551-2916.2011.04574.x
ISSN
0002-7820
Abstract
A crystalline (Na0.5K0.5) NbO3 (NKN) phase was formed for a film grown at 600 degrees C, but a K5.75Nb10.85O30 (KN) second phase was also observed in this film. Formation of the KN phase was due to the evaporation of Na2O. A homogeneous NKN phase was developed in the film grown at 300 degrees C and annealed at 800 degrees C under a Na2O atmosphere. This film exhibited the following good electric and dielectric properties: a high dielectric constant of 237.4 with a dissipation factor of 0.93% at 100 kHz, a low leakage current density of 1.0 x 10(-8) A/cm(2) at 0.1 MV/cm(2), and the high P-r and d(33) values of 21.1 mu C/cm(2) and 64.5 pm/V, respectively.
Files in This Item
There are no files associated with this item.
Appears in
Collections
College of Engineering > Department of Materials Science and Engineering > 1. Journal Articles

qrcode

Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.

Altmetrics

Total Views & Downloads

BROWSE