Adiabatic Shear Banding and Cracking Phenomena Occurring During Cold-Forging Simulation Tests of Plain Carbon Steel Wire Rods by Using a Split Hopkinson's Pressure Bar
DC Field | Value | Language |
---|---|---|
dc.contributor.author | 손석수 | - |
dc.date.accessioned | 2022-04-10T12:40:54Z | - |
dc.date.available | 2022-04-10T12:40:54Z | - |
dc.date.created | 2022-04-08 | - |
dc.date.issued | 2015-11 | - |
dc.identifier.issn | 1598-9623 | - |
dc.identifier.uri | https://scholar.korea.ac.kr/handle/2021.sw.korea/139900 | - |
dc.description.abstract | Adiabatic shear banding and cracking phenomena occurring during cold forging of plain carbon steel wire rods, whose carbon content was varied from 0.2 to 0.8 wt%, were analyzed by forging simulation test using a split Hopkinson's pressure bar. The test results indicated that the 0.2C and 0.3C steels were dynamically compressed without surface defects after the fifth hit, whereas a deep crack was formed along the 45A degrees direction in the 0.8C steel. In all the steels, adiabatic shear bands were formed diagonally inside forging-simulated specimens, and grains were extremely elongated within shear bands. The higher the volume fraction of pearlite was, the easier was the adiabatic shear banding. Particularly in the 0.8C steel, the shear band was white-colored and narrow, along which a long crack was formed. After the spheroidization treatment of the 0.8C steel, adiabatic shear bands or cracks were not found during the forging simulation test as the steel was relatively homogeneously deformed, which indicated that the spheroidization effectively prevented the adiabatic shear banding or cracking. The present forging simulation test plausibly evaluated the cold-forging performance by controlling the number and amount of hit, and provided an important idea on whether the spheroidizat | - |
dc.language | English | - |
dc.language.iso | en | - |
dc.publisher | KOREAN INST METALS MATERIALS | - |
dc.title | Adiabatic Shear Banding and Cracking Phenomena Occurring During Cold-Forging Simulation Tests of Plain Carbon Steel Wire Rods by Using a Split Hopkinson's Pressure Bar | - |
dc.type | Article | - |
dc.contributor.affiliatedAuthor | 손석수 | - |
dc.identifier.doi | 10.1007/s12540-015-5252-6 | - |
dc.identifier.bibliographicCitation | METALS AND MATERIALS INTERNATIONAL, v.21, no.6, pp.991 - 999 | - |
dc.relation.isPartOf | METALS AND MATERIALS INTERNATIONAL | - |
dc.citation.title | METALS AND MATERIALS INTERNATIONAL | - |
dc.citation.volume | 21 | - |
dc.citation.number | 6 | - |
dc.citation.startPage | 991 | - |
dc.citation.endPage | 999 | - |
dc.type.rims | ART | - |
dc.type.docType | Article | - |
dc.description.journalClass | 1 | - |
dc.description.journalRegisteredClass | scie | - |
dc.description.journalRegisteredClass | scopus | - |
dc.description.journalRegisteredClass | kci | - |
dc.subject.keywordAuthor | adiabatic shear banding | - |
dc.subject.keywordAuthor | forging | - |
dc.subject.keywordAuthor | impact test | - |
dc.subject.keywordAuthor | split Hopkinson&apos | - |
dc.subject.keywordAuthor | s pressure bar | - |
dc.subject.keywordAuthor | strain rate | - |
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.
(02841) 서울특별시 성북구 안암로 14502-3290-1114
COPYRIGHT © 2021 Korea University. All Rights Reserved.
Certain data included herein are derived from the © Web of Science of Clarivate Analytics. All rights reserved.
You may not copy or re-distribute this material in whole or in part without the prior written consent of Clarivate Analytics.