Microstructural Analysis of Cracking Phenomenon Occurring During Cold Rolling of (0.1 similar to 0.7)C-3Mn-5Al Lightweight Steels
DC Field | Value | Language |
---|---|---|
dc.contributor.author | 손석수 | - |
dc.date.accessioned | 2022-04-10T20:41:00Z | - |
dc.date.available | 2022-04-10T20:41:00Z | - |
dc.date.created | 2022-04-08 | - |
dc.date.issued | 2015-01 | - |
dc.identifier.issn | 1598-9623 | - |
dc.identifier.uri | https://scholar.korea.ac.kr/handle/2021.sw.korea/139940 | - |
dc.description.abstract | An investigation was conducted into the cracking phenomenon occurring during the cold rolling of lightweight steel plates. Four steels of varying C contents were fabricated and steel plates containing C contents of 0.5 wt% or higher were cracked during the initial stage of the cold rolling. The steels were basically composed of ferrite grains and -carbides in a band shape, but the volume fraction and thickness of kappa-carbide band increased as the C content increased. Microstructural observation of the deformed region of fractured tensile specimens revealed that deformation bands were homogeneously formed in wide areas of ferrite matrix in the steels containing C contents of 0.3 wt% or lower, while kappa-carbide bands were hardly deformed or cracked. In the steels containing high C contents of 0.5 wt% or higher, on the other hand, microcracks were initiated mostly at fine proeutectoid ferrite located within kappa-carbide bands, and were grown further to coalesce with other microcracks to form long cracks. To prevent the cracking, thus, the proeutectoid ferrite should be minimized by the hot rolling in the (alpha+gamma) two phase region. As practical methods, the content of C below 0.5% or Al above 5% was suggested to expand the (alpha+gamma) phase region. | - |
dc.language | English | - |
dc.language.iso | en | - |
dc.publisher | KOREAN INST METALS MATERIALS | - |
dc.title | Microstructural Analysis of Cracking Phenomenon Occurring During Cold Rolling of (0.1 similar to 0.7)C-3Mn-5Al Lightweight Steels | - |
dc.type | Article | - |
dc.contributor.affiliatedAuthor | 손석수 | - |
dc.identifier.doi | 10.1007/s12540-015-1006-8 | - |
dc.identifier.bibliographicCitation | METALS AND MATERIALS INTERNATIONAL, v.21, no.1, pp.43 - 53 | - |
dc.relation.isPartOf | METALS AND MATERIALS INTERNATIONAL | - |
dc.citation.title | METALS AND MATERIALS INTERNATIONAL | - |
dc.citation.volume | 21 | - |
dc.citation.number | 1 | - |
dc.citation.startPage | 43 | - |
dc.citation.endPage | 53 | - |
dc.type.rims | ART | - |
dc.type.docType | Article | - |
dc.description.journalClass | 1 | - |
dc.description.journalRegisteredClass | scie | - |
dc.description.journalRegisteredClass | scopus | - |
dc.description.journalRegisteredClass | kci | - |
dc.subject.keywordAuthor | ferritic lightweight steel | - |
dc.subject.keywordAuthor | fracture | - |
dc.subject.keywordAuthor | phase diagram | - |
dc.subject.keywordAuthor | rolling | - |
dc.subject.keywordAuthor | scanning electron microscopy | - |
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.
(02841) 서울특별시 성북구 안암로 14502-3290-1114
COPYRIGHT © 2021 Korea University. All Rights Reserved.
Certain data included herein are derived from the © Web of Science of Clarivate Analytics. All rights reserved.
You may not copy or re-distribute this material in whole or in part without the prior written consent of Clarivate Analytics.