Effects of aluminum content on cracking phenomenon occurring during cold rolling of three ferrite-based lightweight steel
DC Field | Value | Language |
---|---|---|
dc.contributor.author | 손석수 | - |
dc.date.accessioned | 2022-04-11T07:44:18Z | - |
dc.date.available | 2022-04-11T07:44:18Z | - |
dc.date.created | 2022-04-08 | - |
dc.date.issued | 2013-09 | - |
dc.identifier.issn | 1359-6454 | - |
dc.identifier.uri | https://scholar.korea.ac.kr/handle/2021.sw.korea/139993 | - |
dc.description.abstract | The effects of Al content on cracking phenomena occurring during cold rolling of ferritic lightweight steels were investigated in relation to microstructural modification including x-carbides. Three steels were fabricated, varying the Al content between 4 and 6 wt.%, and the center and edge areas of steel sheets containing 6 wt.% Al were cracked during cold rolling. The three steels were composed of ferrite grains and kappa-carbides in a banded shape, and the overall volume fraction of x-carbide increased with increasing Al content. The shape of lamellar kappa-carbides inside kappa-carbide bands was changed from short and thin to long and thick. Microstructural observation of the deformed region of fractured tensile specimens revealed that deformation bands were homogeneously formed in wide areas of ferrite matrix in the steels containing 4-5 wt.% Al, and x-carbide bands and boundary kappa-carbides were hardly cracked. In the steel containing 6 wt.% Al, however, microcracks were initiated at grain boundary x-carbides and long lamellar kappa-carbides inside x-carbide bands. They led to the center or edge cracking during cold rolling. To prevent or minimize cracking, it was necessary to avoid the lengthening or thickening of lamellar x-carbides. Therefore, it was recommended that t | - |
dc.language | English | - |
dc.language.iso | en | - |
dc.publisher | PERGAMON-ELSEVIER SCIENCE LTD | - |
dc.title | Effects of aluminum content on cracking phenomenon occurring during cold rolling of three ferrite-based lightweight steel | - |
dc.type | Article | - |
dc.contributor.affiliatedAuthor | 손석수 | - |
dc.identifier.doi | 10.1016/j.actamat.2013.06.004 | - |
dc.identifier.bibliographicCitation | ACTA MATERIALIA, v.61, no.15, pp.5626 - 5635 | - |
dc.relation.isPartOf | ACTA MATERIALIA | - |
dc.citation.title | ACTA MATERIALIA | - |
dc.citation.volume | 61 | - |
dc.citation.number | 15 | - |
dc.citation.startPage | 5626 | - |
dc.citation.endPage | 5635 | - |
dc.type.rims | ART | - |
dc.type.docType | Article | - |
dc.description.journalClass | 1 | - |
dc.description.journalRegisteredClass | scie | - |
dc.description.journalRegisteredClass | scopus | - |
dc.subject.keywordAuthor | Calphad | - |
dc.subject.keywordAuthor | Cold rolling | - |
dc.subject.keywordAuthor | Edge crack | - |
dc.subject.keywordAuthor | Ferritic lightweight steel | - |
dc.subject.keywordAuthor | x-Carbide | - |
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.
(02841) 서울특별시 성북구 안암로 14502-3290-1114
COPYRIGHT © 2021 Korea University. All Rights Reserved.
Certain data included herein are derived from the © Web of Science of Clarivate Analytics. All rights reserved.
You may not copy or re-distribute this material in whole or in part without the prior written consent of Clarivate Analytics.