3종의 간접수복용 복합레진의 굴곡강도 비교 및 표면관찰
DC Field | Value | Language |
---|---|---|
dc.contributor.author | 김지환 | - |
dc.contributor.author | 김준태 | - |
dc.contributor.author | 박진영 | - |
dc.contributor.author | 김웅철 | - |
dc.date.accessioned | 2021-09-03T12:01:33Z | - |
dc.date.available | 2021-09-03T12:01:33Z | - |
dc.date.created | 2021-06-17 | - |
dc.date.issued | 2017 | - |
dc.identifier.issn | 1229-3954 | - |
dc.identifier.uri | https://scholar.korea.ac.kr/handle/2021.sw.korea/85254 | - |
dc.description.abstract | Purpose: The purpose of this study was to evaluate flexural strength, composite surface and fractured surface of three different indirect composite resins. Methods: Fifteen bar-shaped specimens (25mm x 2mm x 2mm) were fabricated for each FL group (Flow type and Light curing) and PLP group (Putty type and Light, Pressure curing) and PL group (Putty type and Light curing) according to manufacturer’s instructions and ISO 10477. Fabricated specimens were stored in the distilled water for 24 hours at the temperature of 37℃. Three-point bending strength test was performed to measure flexural strength using universal testing machine at a crosshead speed of 1mm/min (ISO 10477). Surface and fractured surface of specimens were observed by digital microscope. Results were analyzed with Kruskal-wallis tests (α = 0.05). Results: Mean (SD) of three different indirect composite resins were 83.38 (6.67) MPa for FL group, 139.90(16.53) MPa for PLP group and 171.72(16.74) MPa for PL group. Flexural strength were statistically significant (p<0.05). Differences were not observed at fractured surface among three groups. However, many pores over 100㎛ were observed at PL group in observing surface of specimen. Conclusion: Flexural strength of composite resins was affected by second polymerization method and content of inorganic filler. | - |
dc.language | Korean | - |
dc.language.iso | ko | - |
dc.publisher | 대한치과기공학회 | - |
dc.title | 3종의 간접수복용 복합레진의 굴곡강도 비교 및 표면관찰 | - |
dc.title.alternative | Evaluation of Flexural strength and surface porosity of three indirect composite resins | - |
dc.type | Article | - |
dc.contributor.affiliatedAuthor | 김웅철 | - |
dc.identifier.doi | 10.14347/kadt.2017.39.1.9 | - |
dc.identifier.bibliographicCitation | 대한치과기공학회지, v.39, no.1, pp.9 - 16 | - |
dc.relation.isPartOf | 대한치과기공학회지 | - |
dc.citation.title | 대한치과기공학회지 | - |
dc.citation.volume | 39 | - |
dc.citation.number | 1 | - |
dc.citation.startPage | 9 | - |
dc.citation.endPage | 16 | - |
dc.type.rims | ART | - |
dc.identifier.kciid | ART002211257 | - |
dc.description.journalClass | 2 | - |
dc.description.journalRegisteredClass | kci | - |
dc.description.journalRegisteredClass | other | - |
dc.subject.keywordAuthor | composite resins | - |
dc.subject.keywordAuthor | flexural strength | - |
dc.subject.keywordAuthor | heat curing | - |
dc.subject.keywordAuthor | light curing | - |
dc.subject.keywordAuthor | inorganic filler | - |
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.
(02841) 서울특별시 성북구 안암로 14502-3290-1114
COPYRIGHT © 2021 Korea University. All Rights Reserved.
Certain data included herein are derived from the © Web of Science of Clarivate Analytics. All rights reserved.
You may not copy or re-distribute this material in whole or in part without the prior written consent of Clarivate Analytics.