Large-scale production of spherical FeSe2-amorphous carbon composite powders as anode materials for sodium-ion batteries
- Authors
- Park, Gi Dae; Kim, Jung Hyun; Kang, Yun Chan
- Issue Date
- 10월-2016
- Publisher
- ELSEVIER SCIENCE INC
- Keywords
- Metal selenide; Carbon composite; Nanostructure; Sodium ion batteries; Spray drying
- Citation
- MATERIALS CHARACTERIZATION, v.120, pp.349 - 356
- Indexed
- SCIE
SCOPUS
- Journal Title
- MATERIALS CHARACTERIZATION
- Volume
- 120
- Start Page
- 349
- End Page
- 356
- URI
- https://scholar.korea.ac.kr/handle/2021.sw.korea/87434
- DOI
- 10.1016/j.matchar.2016.09.019
- ISSN
- 1044-5803
- Abstract
- A simple two-step method involving a large-scale spray drying process is developed to synthesize metal selenide-amorphous carbon (AC) composite powders (on a kilogram scale) for use as anodes in sodium-ion batteries. The composite powders of iron salt, dextrin, and H2SeO3 are generated in a spray drying process to form the FeSe2-AC composite powders by a one-pot post-treatment process under a reducing atmosphere. The ultrafine FeSe2 single crystals with sizes below 20 nm are uniformly dispersed within the amorphous carbon in the FeSe2-AC composite powders prepared from the spray solution with 30 g L-1 dextrin. The discharge capacities of the powders prepared from spray solutions with 0,10, 20, and 30 g L-1 dextrin for the 150th cycle at a current density of 0.5 A g(-1) are 85,194, 203, 379 mA h g(-1), respectively; their corresponding capacity retentions measured from the second cycle are 19%, 40%, 46%, and 99%. The spherical shape of the FeSe2-AC composite powders is maintained even after 100 cycles. The FeSe2-AC composite powders maintain a high structural stability during repeated sodium insertion and desertion processes, and show superior cycling and rate performances compared to those of the bare FeSe2 powders. (C) 2016 Elsevier Inc. All rights reserved.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > Department of Materials Science and Engineering > 1. Journal Articles
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.