High-performance thin-film protonic ceramic fuel cells fabricated on anode supports with a non-proton-conducting ceramic matrix

초록

A novel strategy to fabricate high-performance thin-film protonic ceramic fuel cells (PCFCs) is introduced by building thin-film PCFC components, including BaCe0.55Zr0.3Y0.15O3-delta (BCZY) electrolytes (1.5 mu m) over anode supports consisting of non-proton-conducting ceramic and metal catalytic phases. Ni-yttria-stabilized zirconia (YSZ) was used as supports in this study, which is superior in terms of its well-established facile fabrication process, along with physical and chemical stability, compared to proton-conducting materials. The Ni-YSZ supports provided a flat and smooth deposition surface that facilitates the deposition of the thin film components. A Ni-BCZY anode (similar to 3 mu m), a dense BCZY electrolyte layer (similar to 1.5 mu m), and a porous Ba0.5Sr0.5Co0.8Fe0.2O3-delta cathode (similar to 2 mu m) were sequentially fabricated over the Ni-YSZ substrates using pulsed laser deposition, followed by post-annealing, and the process was optimized for each component. A fully integrated thin-film PCFC microstructure was confirmed, resulting in high open circuit voltages exceeding 1 V at operating temperatures in the range of 450-650 degrees C. A promising fuel cell performance was obtained using the proposed fuel cell configuration, reaching a peak power density of 742 mW cm(-2) at 650 degrees C.

키워드