Optimizing strength-corrosion properties in sulfuric acid environment via tailoring V-Cr composition in medium-entropy VCrCoNi alloys

초록

The corrosion resistance of VCrCoNi medium-entropy alloys in a 0.5 M H2SO4 solution was investigated by tailoring V and Cr compositions while minimizing microstructural differences. The elemental effects were dis-cussed regarding the formation of the passive film and its subsequent impact on corrosion resistance. The results revealed that an increase in the Cr/V ratio enhances the corrosion resistance by forming a Cr-enriched passive film. However, the elevated ratio negatively affects the mechanical strength, wherein V plays a crucial role. The optimal balance between mechanical strength and corrosion resistance was discussed based on electrochemical measurements and immersion test results.