UV curing-assisted 3D plotting of core-shelled feedrod for macroporous hydroxyapatite scaffolds comprised of microporous hollow filaments

초록

The present study demonstrates the manufacturing of macroporous hydroxyapatite (HA) scaffolds, comprised of microporous hollow filaments with high shape retention, by UV curing-assisted 3D plotting using a feedrod comprised of a photocurable HA shell and a carbon black (CB) core. Two types of scaffolds with different filament interspaces (0.5 mm and 1 mm) were produced by depositing core-shelled filaments extruded through a 1.07mm-diameter nozzle with in situ polymerization process. Both scaffolds exhibited that the hollow HA filaments were produced after the removal of CB core by heat-treatment, while micropores in the HA walls were created as the replica of camphene-camphor crystals. Overall porosity and macroporosity obtained using a camphene-camphor content of 60 vol% increased from 74.3 vol% to 79.3 vol% and from 50.7 vol% and 64.6 vol %, respectively, with an increase in filament interspace sizes from 0.5 mm to 1 mm. Both scaffolds exhibited reasonably high compressive strengths (2.36 - 3.58 MPa) and modulus (68-86 MPa).

키워드