Fabrication and compressive strength of porous hydroxyapatite scaffolds with a functionally graded core/shell structure

초록

A novel type of porous hydroxyapatite (HA) scaffolds with a functionally graded core/shell structure was fabricated by freeze casting HA/camphene slurries with various HA contents into fugitive molds containing a graphite template with three dimensionally interconnected pores for the creation of a highly porous core All the fabricated samples had functionally graded core/shell structures with 3-D periodic pore networks in a core surrounded by a relatively dense shell The overall porosity of the sample decreased from 60 to 38 vol% with increasing HA content in the HA/camphene slurry from 20 to 36 vol% due to a decrease in porosity in both the core and shell regions In addition, the compressive strength was improved remarkably from 12 +/- 11 to 32 +/- 3 0 MPa The in vitro cell test using a pre-osteoblast cell line showed that the samples had good biocompatibility (C) 2010 Elsevier Ltd All rights reserved