Enhanced Heat Resistance of Acrylic Pressure-Sensitive Adhesive by Incorporating Silicone Blocks Using Silicone-Based Macro-Azo-Initiator

초록

To improve the heat resistance of acrylic-based pressure-sensitive adhesive (PSA), silicone-block-containing acrylic PSAs (SPSAs) were synthesized using a polydimethylsiloxane (PDMS)-based macro-azo-initiator (MAI). To evaluate the heat resistance of the PSA films, the probe tack and 90 degrees peel strength were measured at different temperatures. The acrylic PSA showed that its tack curves changed from balanced debonding at 25 degrees C to cohesive debonding at 50 degrees C and exhibited a sharp decrease. However, in the case of SPSA containing 20 wt% MAI (MAI20), the balanced debonding was maintained at 75 degrees C, and its tack value hardly changed with temperature. As the MAI content increased, the peel strength at 25 degrees C decreased due to the microphase separation between PDMS- and acryl-blocks in SPSA, but the shear adhesion failure temperature (SAFT) increased almost linearly from 41.3 to 122.8 degrees C. Unlike stainless steel substrate, SPSA showed improved peel strength on a polypropylene substrate due to its low surface energy caused by PDMS block. Owing to the addition of 20 wt% silicone-urethane dimethacrylate oligomer and 200 mJ/cm(2) UV irradiation dose, MAI20 showed significantly increased 90 degrees peel strength at 25 degrees C (548.3 vs. 322.4 gf/25 mm for pristine MAI20). Its heat resistance under shear stress assessed by shear adhesion failure test (SAFT) exhibited raising in failure temperature to 177.3 degrees C when compared to non-irradiated sample.

키워드