Vat photopolymerization of zirconia suspensions continuously blended by in-line static mixing for strength-gradient zirconia

초록

Vat photopolymerization (VP) of ceramics has demonstrated great promises for manufacturing dental crowns made of partially stabilized zirconia (PSZ) ceramics with excellent dimensional accuracy, outstanding mechanical properties, and good esthetics. However, close mimicking of gradually changing optical translucency of natural teeth still remains challenging. We herein propose functionally graded (FG)-digital light processing (DLP) for manufacturing PSZ objects with gradually varying compositions and mechanical/optical properties using an in-line static mixing system. In this study, 4 mol% and 5 mol% yttria (Y2O3) PSZ, denoted as "4Y-PSZ and 5YPSZ", respectively, were employed as models due to their different mechanical strengths and optical transmittances. Predetermined amounts of 4Y-PSZ and 5Y-PSZ suspensions were fed individually into an in-line static mixer using computer-controlled extrusion systems. This FG-DLP process enabled construction of five gradients with varying 4Y-PSZ/5Y-PSZ compositions (5Y-PSZ content = 0 vol%, 25 vol%, 50 vol%, 75 vol%, and 100 vol %). For uniform blending, as-received 4Y-PSZ and 5Y-PSZ granules were calcined at 1000 degrees C for 1 h and then crushed into fine particles by ball-milling. In addition, UV curing time for different gradients were optimized individually due to different photopolymerization behaviors of 4Y-PSZ and 5Y-PSZ suspensions. After sintering at 1500 degrees C for 2 h, all gradients were almost fully densified and strongly bonded together. When the content of 5YPSZ increased from 0 vol% to 100 vol%, flexural strength decreased from 865 f 80 MPa to 613 f 56 MPa and optical % transmittance increased remarkably from 24.1 f 0.4 % to 31.9 f 0.3 %.

키워드