Growth of boron-doped-ZnO by RF magnetron sputtering for ClGS solar cells
- Hur, Jae-Sung;
- Kim, Jihye;
- Jang, Samseok;
- Song, Jung-Bin;
- Byun, Dongjin;
- 외 3명
WEB OF SCIENCE
7초록
The cell performance of CuIn1-x. GaxSe2 (CIGS) thin-film solar cells fabricated using boron-doped ZnO window layers was evaluated. Boron-doped ZnO was deposited by RF magnetron sputtering using a zinc-oxide target containing 3 wt.% B2O3. Its resistivity was 1.36 x 10(-2) Q-cm and its transmittance was 85 similar to 89 % in the wavelength range from 400 nm to 1000 nm. The transmittance was higher in the near-infrared region than in the other regions. Thus, boron-doped ZnO thin films would be suitable for use as transparent window layers of CIGS solar cells having a higher quantum efficiency on the near-infrared region. The FF and the conversion efficiency were obtained from the J-V measurements and their values were 0.42 and 8.15 %, respectively.
키워드
- 제목
- Growth of boron-doped-ZnO by RF magnetron sputtering for ClGS solar cells
- 저자
- Hur, Jae-Sung; Kim, Jihye; Jang, Samseok; Song, Jung-Bin; Byun, Dongjin; Son, Chang-Sik; Yun, Jae Ho; Yoon, Kyung Hoon
- 발행일
- 2008-07
- 유형
- Article; Proceedings Paper
- 권
- 53
- 호
- 1
- 페이지
- 442 ~ 445