Synthesis of Flower-like Cu-3[MoO4](2)O from Cu-3(MoO4)(2)(OH)(2) and Its Application for Lithium-Ion Batteries: Structure-Electrochemical Property Relationships

초록

Flower-like Cu-3[MoO4](2)O microspheres have been synthesized by using a sequential process from lindgrenite (Cu-3(MoO4)(2)(OH)(2)). Lindgrenite nanoflowers were synthesized through a simpler route by using an aqueous chemical precipitation technique at room temperature without any surfactants or template. Subsequently, 3D flower-like Cu-3[MoO4](2)O microspheres have been synthesized by annealing at 300 degrees C for 2h from lindgrenite (Cu-3(MoO4)(2)(OH)(2)). From the XRD pattern, FTIR spectrum, SEM and TEM analysis, flower-like Cu-3[MoO4](2)O (ca. 5m) microspheres have been obtained, which were assembled from 3-4nm thick nanosheets with an orthorhombic structure. Application of 3D flower-like microspheres as an anode material for lithium-ion batteries (LIBs) has been investigated and the possible electrochemical mechanism is analyzed. Electrochemical characterization of the Cu-3[MoO4](2)O nanoflowers as an anode material for LIBs has exhibited good cycle stability and a high coulombic efficiency during operation. The electrochemical activity was attributed to the unique structure of the Cu-3[MoO4](2)O microspheres, which provide more active sites for Li-ion storage as well as a reduced transfer resistance. This work has explored a simple synthesis strategy for the synthesis of flower-like Cu-3[MoO4](2)O microspheres without templates, additives, or surfactants, which exhibit a basis for not only high electrochemical performance in reversible Li storage, but also cycle stability.

키워드