Threshold voltage shift by controlling Ga in solution processed Si-In-Zn-O thin film transistors

Authors
Choi, Jun YoungKim, SangSigLee, Sang Yeol
Issue Date
1-3월-2012
Publisher
ELSEVIER SCIENCE SA
Keywords
Zinc oxide; Chemical deposition from solution; Threshold voltage; Low temperature
Citation
THIN SOLID FILMS, v.520, no.10, pp.3774 - 3777
Indexed
SCIE
SCOPUS
Journal Title
THIN SOLID FILMS
Volume
520
Number
10
Start Page
3774
End Page
3777
URI
https://scholar.korea.ac.kr/handle/2021.sw.korea/105320
DOI
10.1016/j.tsf.2011.10.212
ISSN
0040-6090
Abstract
The threshold voltage change of solution processed gallium-silicon-indium-zinc oxide (GSIZO) thin film transistors (TFTs) annealed at 200 degrees C has been investigated depending on gallium ratio. GSIZO thin films were formed with various gallium ratios from 0.01 to 1 M ratio. The 30 nm-thick GSIZO film exhibited optimized electrical characteristics, such as field effect mobility (mu(FE)) of 2.2 x 10(-2) cm(2)/V.s, subthreshold swing (S.S) of 0.11 V/dec, and on/off current ratio (I-on/off) of above 10(5). The variation of gallium metal cation has an effect on the threshold voltage (V,h) and the field effect mobility (mu(FE)). The V-th was shifted toward positive direction from -5.2 to -0.4 V as increasing gallium ratio, and mu(FE) was decreased from 2.2 x 10(-2) to 5 x 10(-3) cm(2)/V s. These results indicated that gallium was acted as carrier suppressor by degenerating oxygen vacancy. The electrical property of GSIZO TFTs has been analyzed as a function of the gallium ratio in SIZO system, and it clearly showed that variation of gallium contents could change on the performance of TFTs. (C) 2011 Elsevier BM. All rights reserved.
Files in This Item
There are no files associated with this item.
Appears in
Collections
College of Engineering > School of Electrical Engineering > 1. Journal Articles

qrcode

Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.

Related Researcher

Researcher Kim, Sang sig photo

Kim, Sang sig
공과대학 (전기전자공학부)
Read more

Altmetrics

Total Views & Downloads

BROWSE