Effects of Different Thickness Combinations of Core and Veneer Ceramics on Optical Properties of CAD-CAM Glass-Ceramics

Abstract

The goal of this study was to evaluate the effects of different core and veneer thicknesses on the translucency (T%), average light transmittance (T), translucency parameter (TP), contrast ratio (CR), and spectral reflectance (R) of glass-ceramics using a computer-aided design/computer-aided manufacturing (CAD-CAM) process. In all, 42 specimens (11mm x 11mm) were prepared and divided into six groups (n = 7 for each group). Core materials (IPS e.max CAD; IPS Empress CAD, LT A2 shade) of different thicknesses (0.8, 1.0, and 1.2mm) were fabricated. Each veneer material (thicknesses of 0.7, 0.5, and 0.3mm) was combined with its compatible core ceramic. Each core material was overlapped with its corresponding veneer material to obtain a 1.5-mm thickness by using three different combinations: (0.8+0.7), (1.0+0.5), and (1.2+0.3) mm. A spectrophotometer and color data software were used to measure the T%, T, TP, CR, and R values of each ceramic. The results were statistically analyzed using two-way analysis of variables (ANOVA) and regression analysis (p<0.05). Two-way ANOVA revealed that T%, T, TP, and CR were significantly influenced by the different thicknesses of the core-veneer combinations (p<0.001). At a certain thickness, as the veneer thickness increased and core thickness decreased, T and T% all increased. Regression analysis of the ceramic materials indicated a reduction in T and T% for certain core-veneer combinations. Analysis also revealed that T% and T were all affected by different core-veneer combinations. The T% value was 74.31 for the EM group and 72.81 for the EP group when the thickness of the core was 1.2 mm and the veneer was 0.3 mm. The R value of EM2 was lower than EM1 and EM3. In conclusion, the optical properties were influenced by different core-veneer combinations.