Effects of untransformed ferrite on Charpy impact toughness in 1.8-GPa-grade hot-press-forming steel sheets
- Authors
- 손석수
- Issue Date
- 11월-2017
- Publisher
- ELSEVIER SCIENCE SA
- Keywords
- Charpy impact energy; Hot-press-forming (HPF) steel; Strain localization; Untransformed ferrite
- Citation
- MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, v.707, pp.65 - 72
- Indexed
- SCIE
SCOPUS
- Journal Title
- MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
- Volume
- 707
- Start Page
- 65
- End Page
- 72
- URI
- https://scholar.korea.ac.kr/handle/2021.sw.korea/139804
- DOI
- 10.1016/j.msea.2017.09.027
- ISSN
- 0921-5093
- Abstract
- Hot press forming (HPF) steel sheets are austenitized, press-formed, and rapidly cooled to obtain a martensitic microstructure with an ultra-high strength. When they are insufficiently austenitized, their microstructures might contain a small amount of untransformed ferrite, which can deteriorate impact toughness as well as strength, but its causes and relevant fracture mechanisms have not been clearly verified yet. In this study, thus, 1.8-GPa-grade HPF sheets were austenitized at various temperature and time, and their tensile and Charpy impact test results were analyzed in relation with untransformed ferrite and its effect on fracture mechanisms. In the HPF sheets containing the untransformed ferrite, voids were formed mostly at ferrite/martensite interfaces, and were grown and propagated linearly to form a cleavage crack, whereas deformation bands were well developed without voids or cracks in the non-ferrite-containing sheets. The highly localized strains accommodated in the soft ferrite made ferrite/martensite interfaces or ferrite itself work as fracture initiation sites, which led to the brittle fracture and consequently to the deterioration of impact energy. This result can provide an important idea for optimization of austenitization conditions demanded for ultra-high s
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > Department of Materials Science and Engineering > 1. Journal Articles
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.