Light sintering of ultra-smooth and robust silver nanowire networks embedded in poly(vinyl-butyral) for flexible OLED
- Authors
- Lee, Dong Jun; Oh, Youngsu; Hong, Jae-Min; Park, Young Wook; Ju, Byeong-Kwon
- Issue Date
- 21-Sep-2018
- Publisher
- NATURE PUBLISHING GROUP
- Citation
- SCIENTIFIC REPORTS, v.8
- Indexed
- SCIE
SCOPUS
- Journal Title
- SCIENTIFIC REPORTS
- Volume
- 8
- URI
- https://scholar.korea.ac.kr/handle/2021.sw.korea/73071
- DOI
- 10.1038/s41598-018-32590-0
- ISSN
- 2045-2322
- Abstract
- A conductive, uniform, and ultra-smooth flexible transparent composite film is produced by embedding silver nanowires (AgNWs) into poly(vinyl-butyral) (PVB) without pressure or high-temperature annealing. The adhesion of AgNWs was greatly improved by embedding them in PVB, and surface roughness and sheet resistance (R-s) improvements were achieved through the use of the intense pulsed light (IPL) method, which welds the interconnections among AgNWs in a short time without heat or pressure treatment. The sheet resistance of PVB/AgNWs with the IPL(PAI) composite film reaches 12.6 ohm/sq with a transmittance of 85.7% (at 550 nm); no clear changes in the sheet resistance are observed after a substrate bending and tape test, suggesting excellent flexibility. In the case of PAI, the change in sheet resistance was only 2.6% after a 2,000-bend test, and the resulting bending radius was less than 1 mm. When IPL was exposed to PVB/AgNWs, the figure of merit was 2.36 times higher than that without exposure. Finally, flexible OLEDs using PAI exhibited comparable or higher electroluminescent characteristics than other devices with well-known flexible electrodes-including indium-zinc-oxide on polymer plastic-which is a promising discovery for flexible optoelectronic applications.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > School of Electrical Engineering > 1. Journal Articles
![qrcode](https://api.qrserver.com/v1/create-qr-code/?size=55x55&data=https://scholar.korea.ac.kr/handle/2021.sw.korea/73071)
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.