Control over electrically bistable properties of layer-by-layer-assembled polymer/organometal multilayers
- Authors
- Cheong, Sanghyuk; Kim, Younghoon; Ryu, Sook Won; Cho, Jinhan
- Issue Date
- 4월-2016
- Publisher
- NATURE PUBLISHING GROUP
- Citation
- POLYMER JOURNAL, v.48, no.4, pp.481 - 486
- Indexed
- SCIE
SCOPUS
- Journal Title
- POLYMER JOURNAL
- Volume
- 48
- Number
- 4
- Start Page
- 481
- End Page
- 486
- URI
- https://scholar.korea.ac.kr/handle/2021.sw.korea/89015
- DOI
- 10.1038/pj.2016.4
- ISSN
- 0032-3896
- Abstract
- We demonstrate that nonvolatile memory devices can be prepared using electrostatic layer-by-layer (LbL)-assembled nanocomposite films, and additionally that their performance can be easily enhanced by an additional insertion of charge trap elements within the films. For this study, cationic poly(allylamine hydrochloride) (PAH) and anionic titania precursors (titanium (IV) bis(ammonium lactato) dihydroxide, TALH) were used for the preparation of electrostatic LbL-assembled nanocomposite films on a Pt-coated silicon wafer. The formed multilayer nanocomposites were converted into the transition metal oxide films (that is, TiOx nanocomposites) after thermal annealing at 450 degrees C, and then, the top electrodes were deposited onto the TiOx films to complete the device fabrication. When external bias was applied to the devices, these TiOx-based devices displayed bipolar resistive switching property with an ON/OFF current ratio of similar to 10. However, the insertion of anionic graphene oxide (GO) nanosheets into the PAH/TALH multilayers produced GO-incorporated TiOx films after thermal annealing, which exhibited memory performance with a high ON/OFF current ratio of similar to 10(4). Furthermore, we demonstrate that the switching mechanism of GO-incorporated TiOx devices can be explained by the charge trap model.
- Files in This Item
- There are no files associated with this item.
- Appears in
Collections - College of Engineering > Department of Chemical and Biological Engineering > 1. Journal Articles
Items in ScholarWorks are protected by copyright, with all rights reserved, unless otherwise indicated.